The slump cone, also known as Abrams cone, is used to measure workability of fresh concrete
Standards AASHTO T119 ASTM C143 EN 12350-2
This test method is used to measure the consistency of stiff to extremely dry concrete.
Standards EN 12350-3 ASTM C1170 ASTM C1176
This test method is used to measure the consistency of stiff to extremely dry concrete. Consistency is measured as the time required for a given mass of concrete to be consolidated by vibrating in a cylindrically shaped mould. The small vibrating table operates at a fixed amplitude and frequency.
Versions available:
The operating principle is practically identical and the units differ from one to the other in the shape of the container and swivel arm with surcharge weight. The 50 lb (22.7 kg) surcharge weight required by ASTM C1170-Procedure A, which is part of the 54-C0195/C unit, can be replaced by the 27,5 lb (12,5 kg) sliding weight to Procedure B and/or by the 20 lb (9 kg) sliding weight conforming to ASTM C1176 (see accessories). Otherwise it’s available the equipment conforming to ASTM C1176 supplied along with 20lb (9kg) surcharge weight. In the EN model the weight of the moving part is 2.75 kg.
Vebè consistometer conforming to EN 12350-3
230V, 50 Hz, 1 ph
Vebè consistometer conforming to EN 12350-3
220V, 60 Hz, 1 ph
Vebè consistometer conforming to EN 12350-3
110V, 60 Hz, 1 ph
The apparatus consists of a double wooden table measuring 700x700 mm hinged at one side.
Standards EN 12350-5
The apparatus consists of a double wooden table measuring 700×700 mm hinged at one side. The top table is covered with an inscribed metal plate 2 mm thick: The steel cone, part of the apparatus, has a top dia. of 130 mm a base dia. of 200 mm and is 200 mm high. Complete with wooden tamping rod. All metal parts are protected against corrosion.
Weight approx.: 30 kg
The apparatus consists of two conical hoppers having a hinged trap door attached to the lower...
Standards BS 1881:103
Used to verify the homogeneity of concrete in relation to its workability or plasticity.
Standards NF P18-452
Used to verify the homogeneity of concrete in relation to its workability or plasticity. This test method has particular application for concretes containing chemical admixtures.
The apparatus consists of a metal box divided into two parts and fit with an electrical vibrator system. During operation the concrete is poured into the first section of the box and then the dividing plate is removed. The vibrator is immediately switched on and the time is recorded when the concrete has spread uniformly across the whole box.
This device is used to determine the workability and degree of compaction of fresh concrete
Standards ASTM C1362
This device is used to determine the workability and degree of compaction of fresh concrete after being placed in the forms. It can be used for in-situ measurements or inside test moulds and forms. Results can be correlated against the slump test.
The operation is very simple: insert the tester into the concrete up to the level of the disc, after 60 seconds, a measuring rod in lowered onto the surface of the concrete and the K-slump is read directly on a scale. The calibrated hollow tube has a dia. of 20 mm.
This method is used to determine the penetration of a hemispherical metal weight into fresh concrete
Standards ASTM C360 ASTM D6024
This method is used to determine the penetration of a hemispherical metal weight into freshly mixed concrete, which is related to the workability of the concrete.
The apparatus consists of a cylinder with one end having a hemispherical shape and the other end fit with a graduated handle. The weight assembly is lowered through a frame into the concrete and the penetration measured.
The apparatus consists of a metal box with handles. Dimensions: 200x200x400 (h) mm Wei
Standards EN 12350-4
The apparatus consists of a metal box with handles.